Polyolefin composition

ABSTRACT

A polyolefin composition made from or containing:
     A) 5-35% by weight of a propylene homopolymer;   B) 20-50% by weight of an ethylene homopolymer; and   C) 30-60% by weight of a terpolymer of ethylene, propylene and 1-butene derived units.

FIELD OF THE INVENTION

In general, the present disclosure relates to the field of chemistry. More specifically, the present disclosure relates to polymer chemistry. In particular, the present disclosure relates to polyolefin compositions, preparation of the polyolefin compositions, and the use of the polyolefin compositions as impact modifiers in polyolefin blends.

BACKGROUND OF THE INVENTION

In some instances, impact modifier compositions are made from or containing an amorphous olefin copolymer. In some instances, impact modifier compositions are added in polyolefin compositions to enhance the impact resistance. In some instances, the resulting polyolefin compositions are used in automotive applications.

In some instances, an impact modifier composition is added to different kinds of polyolefins, thereby providing a final composition ready for production of articles such as automobile bumpers.

SUMMARY OF THE INVENTION

In a general embodiment, the present disclosure provides a polyolefin composition made from or containing:

A) 5-35% by weight of a propylene homopolymer containing 10% by weight or less of a fraction soluble in xylene at 25° C. (XS_(A)), the amount of the fraction XS_(A) being referred to the weight of (A);

B) 20-50% by weight of an ethylene homopolymer containing 5% by weight or less of a fraction soluble in xylene at 25° C. (XS_(B)), the amount of the fraction XS_(B) being referred to the weight of (B); and

C) 30-60% by weight of a terpolymer, wherein the terpolymer contains ethylene, propylene and 1-butene derived units containing from 45% to 65% by weight of ethylene units and from 15% to 38% by weight of 1-butene units; and containing from 30% to 85% by weight of a fraction soluble in xylene at 25° C. (XS_(C)), the amount of the ethylene units, the 1-butene units, and the fraction XS_(C) being referred to the weight of (C);

the amounts of (A), (B) and (C) being referred to the total weight of (A)+(B)+(C), the sum of the amount of (A)+(B)+(C) being 100 wt %.

DETAILED DESCRIPTION OF THE INVENTION

In some embodiments, the present disclosure provides a polyolefin composition made from or containing:

A) 5-35% by weight; alternatively 10-30% by weight; alternatively 15-23% by weight, of a propylene homopolymer containing 10% by weight or less, alternatively 8 wt % or less, alternatively 6 wt % or less, of a fraction soluble in xylene at 25° C. (XS_(A)), the amount of the fraction XS_(A) being referred to the weight of (A);

B) 20-50% by weight; alternatively 25-45% by weight; alternatively 30-40% by weight, of an ethylene homopolymer containing 5% by weight or less; alternatively 4 wt % or less; alternatively 3 wt % or less, of a fraction soluble in xylene at 25° C. (XS_(B)), the amount of the fraction XS_(B) being referred to the weight of (B); and

C) 30-60% by weight; alternatively 35-55% by weight; alternatively 40-50% by weight, of a terpolymer of ethylene, propylene and 1-butene containing from 45% to 65% by weight, alternatively from 48% to 62% by weight; alternatively from 50% to 60% by weight, of ethylene units; and from 15% to 38%; alternatively from 18% to 33% by weight, alternatively from 20% to 30% by weight, of 1-butene units; and containing from 30% to 85%; alternatively from 35% to 50% by weight of a fraction soluble in xylene at 25° C. (XS_(C)), the amount of the ethylene units, the 1-butene units, and the fraction XS_(C) being referred to the weight of (C);

the amounts of (A), (B) and (C) being referred to the total weight of (A)+(B)+(C), the sum of the amount of (A)+(B)+(C) being 100.

In some embodiments, component (A) has a melt flow rate (230° C./2.16 kg) ranging between 50 and 200 g/10 min; alternatively between 80 and 170 g/10 min.

In some embodiments, the ethylene homopolymer (B) contains up to 5% by weight, alternatively up to 3% by weight, of comonomer units. In some embodiments, the comonomer units are derived from one or more comonomers selected from C₃ to C₈ alpha-olefins. In some embodiments, the alpha-olefin comonomers are selected from the group consisting of propylene, butene-1, pentene-1,4-methylpentene-1, hexene-1 and octene-1. In some embodiments, the alpha-olefin comonomers are selected from the group consisting of propylene and 1-butene. In some embodiments, the ethylene homopolymer (B) does not contain additional comonomer units.

In some embodiments, the ethylene homopolymer (B) has a melt flow rate (230° C./2.16 kg) between 0.1 and 50 g/10 min., alternatively between 0.1 and 30 g/10 min; alternatively between 0.1 and 10 g/10 min.

In some embodiments, the ethylene homopolymer (B) has a density (determined according to ISO 1183 at 23° C.) of from 0.940 to 0.965 g/cm³.

In some embodiments, components (A)+(B) blended together have a melt flow rate (230° C./2.16 kg) between 0.1 and 70 g/10 min., alternatively between 1 and 50 g/10 min; alternatively between 8 and 40 g/10 min.

In some embodiments, the polyolefin composition (A)+(B)+(C) has a melt flow rate (230° C./2.16 kg) between 0.5 to 25 g/10 min, alternatively from 0.8 to 20.0 g/10 min; alternatively from 1.0 to 18.0 g/10 min.

In some embodiments, the xylene soluble fraction at 25° C. of the polyolefin composition (A+B+C) has an intrinsic viscosity [η] (measured in tetrahydronaphthalene at 135° C.) between 2.4 and 3.8 dl/g, alternatively between 2.4 and 3.5 dl/g, alternatively between 2.5 and 3.3 dl/g.

As used herein, the term “copolymer” refers to a polymer containing two kinds of comonomers, such as propylene and ethylene or ethylene and 1-butene. As used herein, the term “terpolymer” refers to a polymer containing three kinds of comonomers, such as propylene, ethylene and 1-butene.

In some embodiments, the polyolefin composition is prepared by a sequential polymerization, including at least three sequential steps, wherein components (A), (B) and (C) are prepared in separate subsequent steps, operating in each step, except the first step, in the presence of the polymer formed and the catalyst used in the preceding step. In some embodiments, the catalyst is added in the first step and not in subsequent steps. In some embodiments, the catalyst remains active for the subsequent steps.

In some embodiments, the polymerization is a continuous process. In some embodiments, the polymerization is a batch process. In some embodiments, the polymerization is carried out in liquid phase, in the presence or not of inert diluent, or in gas phase, or by mixed liquid-gas techniques. In some embodiments, the polymerization is carried out in gas phase.

In some embodiments, the temperature for the polymerization steps is from 50 to 100° C. In some embodiments, the pressure for the polymerization steps is atmospheric or higher.

In some embodiments, the molecular weight is regulated. In some embodiments, the molecular weight regulator is hydrogen.

In some embodiments, the polymerizations are carried out in the presence of a Ziegler-Nana catalyst. In some embodiments, a Ziegler-Natta catalyst is made from or containing the product of the reaction of an organometallic compound of group 1, 2 or 13 of the Periodic Table of elements with a transition metal compound of groups 4 to 10 of the Periodic Table of Elements (new notation). In some embodiments, the transition metal compound is selected from the group consisting of compounds of Ti, V, Zr, Cr and Hf. In some embodiments, the transition metal compound is supported on MgCl₂.

In some embodiments, the catalysts are made from or containing the product of the reaction of the organometallic compound of group 1, 2 or 13 of the Periodic Table of elements, with a solid catalyst component made from or containing a Ti compound and an electron donor compound supported on MgCl₂.

In some embodiments, the organometallic compounds are aluminum alkyl compounds.

In some embodiments, the polymer composition is obtained by using a Ziegler-Natta polymerization catalyst, alternatively a Ziegler-Natta catalyst supported on MgCl₂, alternatively a Ziegler-Natta catalyst made from or containing the product of reaction of:

1) a solid catalyst component made from or containing a Ti compound and an electron donor (internal electron-donor) supported on MgCl₂;

2) an aluminum alkyl compound (cocatalyst); and, optionally,

3) an electron-donor compound (external electron-donor).

In some embodiments, the solid catalyst component (1) contains as electron-donor a compound selected from the group consisting of ethers, ketones, lactones, compounds containing N, P and/or S atoms, and mono- and dicarboxylic acid esters.

In some embodiments, the catalysts are as described in U.S. Pat. No. 4,399,054 and European Patent No. 45977.

In some embodiments, the electron-donor compounds are selected from the group consisting of phthalic acid esters and succinic acid esters. In some embodiments, the phthalic acid ester is diisobutyl phthalate.

In some embodiments, the succinic acid esters are represented by the formula (I):

wherein the radicals R₁ and R₂, equal to or different from each other, are a C₁-C₂₀ linear or branched alkyl, alkenyl, cycloalkyl, aryl, arylalkyl or alkylaryl group, optionally containing heteroatoms; the radicals R₃ to R₆ equal to or different from each other, are hydrogen or a C₁-C₂₀ linear or branched alkyl, alkenyl, cycloalkyl, aryl, arylalkyl or alkylaryl group, optionally containing heteroatoms. In some embodiments, the radicals R₃ to R₆ are joined to the same carbon atom and linked together to form a cycle.

In some embodiments, R₁ and R₂ are C₁-C₈ alkyl, cycloalkyl, aryl, arylalkyl and alkylaryl groups. In some embodiments, R₁ and R₂ are selected from primary alkyls, alternatively branched primary alkyls. In some embodiments, R₁ and R₂ groups are selected from the group consisting of methyl, ethyl, n-propyl, n-butyl, isobutyl, neopentyl, and 2-ethylhexyl. In some embodiments, R₁ and R₂ groups are selected from the group consisting of ethyl, isobutyl, and neopentyl.

In some embodiments, R₃ to R₅ are hydrogen and R₆ is a branched alkyl, cycloalkyl, aryl, arylalkyl and alkylaryl radical having from 3 to 10 carbon atoms. In some embodiments, at least two radicals from R₃ to R₆ are different from hydrogen and selected from C₁-C₂₀ linear or branched alkyl, alkenyl, cycloalkyl, aryl, arylalkyl or alkylaryl group, optionally containing heteroatoms. In some embodiments, the two radicals different from hydrogen are linked to the same carbon atom. In some embodiments, R₃ and R₅ are different from hydrogen and linked to different carbon atoms. In some embodiments, R₄ and R₆ are different from hydrogen and linked to different carbon atoms.

In some embodiments, the electron-donors are the 1,3-diethers described in European Patent Application Nos. EP-A-361 493 and 728769.

In some embodiments, cocatalysts (2) are trialkyl aluminum compounds. In some embodiments, the trialkyl aluminum compounds are selected from the group consisting of Al-triethyl, Al-triisobutyl and Al-tri-n-butyl.

In some embodiments, the electron-donor compounds (3) used as external electron-donors (added to the Al-alkyl compound) are selected from the group consisting of aromatic acid esters, heterocyclic compounds, and silicon compounds containing at least one Si—OR bond (where R is a hydrocarbon radical). In some embodiments, the aromatic acid esters are alkylic benzoates. In some embodiments, the heterocyclic compounds are selected from the group consisting of 2,2,6,6-tetramethylpiperidine and 2,6-diisopropylpiperidine.

In some embodiments, the silicon compounds have the formula R¹ _(a)R² _(b)Si(OR³)_(c), where a and b are integer numbers from 0 to 2, c is an integer from 1 to 3 and the sum (a+b+c) is 4; R¹, R² and R³ are alkyl, cycloalkyl or aryl radicals with 1-18 carbon atoms optionally containing heteroatoms.

In some embodiments, the silicon compounds are selected from the group consisting of (tert-butyl)₂Si(OCH₃)₂, (cyclohexyl)(methyl)Si (OCH₃)₂, (phenyl)₂Si(OCH₃)₂ and (cyclopentyl)₂Si(OCH₃)₂.

In some embodiments, the 1,3-diethers are used as external donors. In some embodiments, the internal donor is a 1,3-diether and the external donor is omitted.

In some embodiments, the catalysts are precontacted with small quantities of olefin (prepolymerization), maintaining the catalyst in suspension in a hydrocarbon solvent, and polymerizing at temperatures from room to 60° C., thereby producing a quantity of polymer from 0.5 to 3 times the weight of the catalyst.

In some embodiments, the operation takes place in liquid monomer, producing a quantity of polymer up to 1000 times the weight of the catalyst.

In some embodiments, the polyolefin composition of the present disclosure is used as an impact modifier in polyolefin blend for molding applications, alternatively for the production of injection-molded articles. In some embodiments, the polyolefin composition also is used for films or molded articles.

In some embodiments, the polyolefin composition has a very low value of Scratch resistance (10 N),N127 (measured according to GME 60280). In some embodiments and as used herein, “very low value of Scratch resistance” refers to lower than 2.0 dL; alternatively lower than 1.8 dL; alternatively lower than 1.7 dL.

In some embodiments, the polyolefin composition is further made from or containing additives. In some embodiments, the additives are selected from the group consisting of mineral fillers, fibers, colorants and stabilizers. In some embodiments, the mineral fillers are selected from the group consisting of talc, CaCO₃, silica, clays, diatomaceaous earth, titanium oxide and zeolites. In some embodiments, the silica is wollastonite (CaSiO₃). In some embodiments, the mineral filler is in particle form having an average diameter ranging from 0.1 to 5 micrometers. In some embodiments, the polyolefin composition is further made from or containing fibers. In some embodiments, the fibers are glass fibers, carbon fibers, metallic fibers, or ceramic fibers.

The following examples are given to illustrate, but not limit the present disclosure.

EXAMPLES Characterizations

Xylene-Soluble (XS) Fraction at 25° C.

Solubility in xylene: Determined as follows:

2.5 g of polymer and 250 ml of xylene were introduced into a glass flask equipped with a refrigerator and a magnetic stirrer. The temperature was raised in 30 minutes up to the boiling point of the solvent. The resulting clear solution was then kept under reflux and stirred for 30 minutes. The closed flask was then kept for 30 minutes in a bath of ice and water, then in a thermostatic water bath at 25° C. for 30 minutes. The resulting solid was filtered on quick filtering paper. 100 ml of the filtered liquid were poured in a pre-weighed aluminum container, which was heated on a heating plate under nitrogen flow, thereby removing the solvent by evaporation. The container was then kept in an oven at 80° C. under vacuum until a constant weight was obtained. The weight percentage of polymer soluble in xylene at room temperature was then calculated.

The content of the xylene-soluble fraction is expressed as a percentage of the original 2.5 grams and then, by the difference (complementary to 100%), the xylene insoluble percentage (%);

XS of components B) and C) were calculated by using the formula:

XS _(tot) =WaXS _(A) +WbXS _(B) +WcXS _(C)

wherein Wa, Wb and We were the relative amount of components A, B and C, respectively, and (A+B+C=1).

Melt Flow Rate (MFR)

Measured according to ISO 1133 at 230° C. with a load of 2.16 kg, unless otherwise specified.

Intrinsic Viscosity (IV)

The sample was dissolved in tetrahydronaphthalene at 135° C. and then poured into a capillary viscometer. The viscometer tube (Ubbelohde type) was surrounded by a cylindrical glass jacket; this setup allowed for temperature control with a circulating thermostatic liquid. The downward passage of the meniscus was timed by a photoelectric device.

The passage of the meniscus in front of the upper lamp started the counter which had a quartz crystal oscillator. The counter stopped as the meniscus passed the lower lamp. The efflux time was registered and converted into a value of intrinsic viscosity through Huggins' equation (Huggins, M. L., J. Am. Chem. Soc., 1942, 64, 2716), using the flow time of the pure solvent at the same experimental conditions (same viscometer and same temperature). A single polymer solution was used to determine [η].

Comonomer (C₂ and C₄) Content

The content of comonomers was determined by infrared (IR) spectroscopy by collecting the IR spectrum of the sample vs. an air background with a Fourier transform infrared spectrometer (FTIR). The instrument data acquisition parameters were:

-   -   purge time: 30 seconds minimum     -   collect time: 3 minutes minimum     -   apodization: Happ-Genzel     -   resolution: 2 cm-1.

Sample Preparation—Using a hydraulic press, a thick sheet was obtained by compression molding about 1 g of sample between two aluminum foil sheets. A small portion was cut from the resulting sheet to mold a film. The film thickness was set to have a maximum absorbance of the CH2 absorption band at ˜720 cm-1 of 1.3 a.u. (% Transmittance>5%). The molding conditions were carried out at a temperature of about 180±10° C. (356° F.) and a pressure of about 10 kg/cm2 (142.2 psi) for about one minute. The pressure was then released. The sample was removed from the press and cooled to room temperature. The spectrum of the pressed film sample was recorded as a function of absorbance vs. wavenumbers (cm-1). The following measurements were used to calculate ethylene (C2) and 1-butene (C4) contents:

Area (At) of the combination absorption bands between 4482 and 3950 cm-1, which was used for spectrometric normalization of film thickness.

Area (AC2) of the absorption band due to methylenic sequences (CH2 rocking vibration) in a range of 660-790 cm-1 after a proper digital subtraction of an isotactic polypropylene (IPP) and a C2C4 references spectrum.

The factor of subtraction (FCRC4) between the spectrum of the polymer sample and the C2C4 reference spectrum: The reference spectrum was obtained by performing a digital subtraction of a linear polyethylene from a C2C4 copolymer to extract the C4 band (ethyl group at ˜771 cm-1).

The ratio AC2/At was calibrated by analyzing ethylene-propylene standard copolymers of compositions determined by NMR spectroscopy.

The assignments of the spectra, triad distribution and composition were made according to Kakugo (“Carbon-13 NMR determination of monomer sequence distribution in ethylene-propylene copolymers prepared with δ-titanium trichloride-diethylaluminum chloride,” M. Kakugo, Y. Naito, K. Mizunuma and T. Miyatake, Macromolecules, 1982, 15, 1150).

To calculate the ethylene (C2) and 1-butene (C4) content, calibration curves were obtained by using reference samples of ethylene and 1-butene that were detectable by 13C NMR.

Calibration for ethylene—A calibration curve was obtained by plotting AC2/At versus ethylene molar percent (% C2m), and the coefficients aC2, bC2 and cC2 were then calculated via linear regression.

Calibration for 1-butene—A calibration curve was obtained by plotting FCRC4/At versus butane molar percent (% C4m), and the coefficients aC4, bC4 and CC4 were then calculated via linear regression.

The spectra of the samples were recorded and then (At), (AC2) and (FCRC4) were calculated.

The ethylene content (% molar fraction C2m) of the sample was calculated as follows:

${\%\mspace{14mu} C\; 2m} = {{- b_{C\; 2}} + \frac{\sqrt{b_{C\; 2}^{2} - {4 \cdot a_{C\; 2} \cdot \left( {c_{C\; 2} - \frac{A_{C\; 2}}{A_{t}}} \right)}}}{2 \cdot a_{C\; 2}}}$

The 1-butene content (% molar fraction C4m) of the sample was calculated as follows:

${\%\mspace{14mu} C\; 4m} = {{- b_{C\; 4}} + \frac{\sqrt{b_{C\; 4}^{2} - {4 \cdot a_{C\; 4} \cdot \left( {c_{C\; 4} - \frac{A_{C\; 4}}{A_{t}}} \right)}}}{2 \cdot a_{C\; 4}}}$

where aC4, bC4, cC4 aC2, bC2, cC2 were the coefficients of the two calibrations.

Changes from mol % to wt % were calculated by using molecular weights of the compound(s).

Amount (wt %) of comonomer of components B-C were calculated by using the following relationship:

Com_(tot) =WaCom_(A) +WbCom_(B) +WcCom_(C)

wherein Wa, Wb and We were the relative amount of components A, B and C, respectively, and (A+B+C=1).

Comet, COMA, COMB and ComC were the amounts of comonomer in the total composition (tot) and components A-C.

Example 1—Preparation of the Polyolefin Composition

Catalyst Precursor:

The solid catalyst component used in the polymerization was a Ziegler-Natta catalyst component supported on magnesium chloride (MgCl₂) containing titanium and diisobutylphthalate as an internal donor. An initial amount of microspheroidal MgCl₂.2.8C₂H₅OH was prepared according to Example 2 of U.S. Pat. No. 4,399,054, but operating at 3,000 rpm instead of 10,000 rpm. The resulting adduct was subjected to thermal dealcoholation at increasing temperatures from 30-130° C. in a nitrogen current until the molar alcohol content per mol of Mg was about 1.16. Into a 1000 mL four-necked round flask, purged with nitrogen, 500 mL of TiCl₄ were introduced at 0° C. While stirring, 30 grams of the microspheroidal MgCl₂.1.16C₂H₅OH adduct were added. The temperature was raised to 120° C. and maintained for 60 minutes. During the temperature increase, an amount of diisobutylphthalate was added to produce a Mg/diisobutylphthalate molar ratio of about 18. After 60 minutes, the stirring was stopped, the liquid was siphoned off, and the treatment with TiCl4 was repeated at 100° C. for 1 hour in the presence of an amount of diisobutylphthalate to produce a Mg/diisobutylphthalate molar ratio of about 27. The stirring was stopped. The liquid was siphoned off, and the treatment with TiCl₄ was repeated at 100° C. for 30 min. After sedimentation and siphoning at 85° C., the solid was washed six times with anhydrous hexane (6×100 ml) at 60° C.

Catalyst System and Prepolymerization:

Before introducing the solid catalyst component into the polymerization reactors, the solid catalyst component was contacted at 30° C. for 9 minutes with aluminum triethyl (TEAL) and dicyclopentyldimethoxysilane (DCPMS) at a TEAL/DCPMS weight ratio of about 15 and in such a quantity that the TEAL/solid catalyst component weight ratio was about 4.

The catalyst system was then subjected to prepolymerization by suspending the catalyst system in liquid propylene at 50° C. for about 75 minutes before introducing the catalyst system into the first polymerization reactor.

Polymerization

The polymerization was carried out in continuous mode in a series of three gas-phase reactors equipped with devices to transfer the product from the first reactor to the second reactor. A propylene-based polymer (A) was produced in the first gas phase polymerization reactor by feeding the prepolymerized catalyst system, hydrogen (the molecular weight regulator) and propylene, with the components in a gas state, in a continuous and constant flow. The propylene-based polymer (A) coming from the first reactor was discharged in a continuous flow and, after having been purged of unreacted monomers, introduced, in a continuous flow, into the second gas phase reactor, together with quantitatively constant flows of hydrogen and ethylene, with the components in a gas state. In the second reactor, a copolymer of ethylene (B) was produced. The product coming from the second reactor was discharged in a continuous flow and, after having been purged of unreacted monomers, introduced, in a continuous flow, into the third gas phase reactor, together with quantitatively constant flows of hydrogen, ethylene and propylene, with the components in a gas state. In the third reactor, an ethylene-propylene polymer (C) was produced. Polymerization conditions, molar ratio of the reactants and compositions of the resulting copolymers are shown in Table 1. The polymer particles exiting the third reactor were subjected to a steam treatment to remove the reactive monomers and volatile substances and then dried. Thereafter, the polymer particles were mixed with a stabilizing additive composition in a twin screw extruder BerstorffZE 25 (length/diameter ratio of screws: 34) and extruded under a nitrogen atmosphere in the following conditions:

Rotation speed: 250 rpm;

Extruder output: 15 kg/hour;

Melt temperature: 245° C.

The stabilizing additive composition was made from or containing the following components:

-   -   0.1% by weight of Irganox® 1010;     -   0.1% by weight of Irgafos® 168; and     -   0.04% by weight of DHT-4A (hydrotalcite);

where the percentage amounts refer to the total weight of the polymer and stabilizing additive composition.

Irganox® 1010 was 2,2-bis[3-[5-bis(1,1-dimethylethyl)-4-hydroxyphenyl)-1-oxopropoxy]methyl]-1,3-propanediyl-3,5-bis(1,1-dimethylethyl)-4-hydroxybenzene-propanoate, and Irgafos® 168 was tris(2,4-di-tert.-butylphenyl)phosphite. The characteristics of the polymer composition, reported in Table 2, were obtained from measurements carried out on the extruded polymer, which constituted a stabilized ethylene polymer composition.

TABLE 1 Polymerization conditions Example Example 1 Comp. 2 1^(st) Reactor—component (A) Temperature ° C. 60 60 Pressure barg 16 16 H₂/C₃— mol. 0.16 0.20 Split wt % 20 20 Xylene soluble of (A) (XS_(A)) wt % 4.6 4.5 2^(nd) Reactor—component (B) Temperature ° C. 80 80 Pressure barg 18 17 H₂/C₂— mol. 1.04 0.26 C₄—/(C₂— + C₄—) mol. 0 0 C₂—/(C₂— + C₃—) mol. 0.83 0.90 Split wt % 35 35 C₂— content of B * wt % 100 100 C₄— content of B * wt % 0 0 3rd Reactor—component (C) Temperature ° C. 67 65 Pressure barg 16 16 H₂/C₂— mol. 0.16 0.15 C₃—/(C₂— + C₃—) mol. 0.42 0.41 C₄—/(C₂— + C₄—) 0.41 0 Split wt % 45 45 Notes: C₂— = ethylene (IR); C₃— = propylene (IR); C₄— = 1-butene (IR); split = amount of polymer produced in the concerned reactor. * Calculated values.

The features of the polymer of Example 1 and comparative example 2 are reported in Table 2.

TABLE 2 Example 1 Comp 2 component A C₂ content wt % 0 0 XSA wt % 4.6 4.3 MFR g/10 min 110 100 split wt % 20 20 component B XSB* wt % 1.7 1.7 C₂ content* wt % 100 100 split wt % 35 35 MFR g/10 min 17.4 4.5 Component C XSC* wt % 39.5 39.8 C₂ content* wt % 55.0 54.2 C₄ content* wt % 23 0 split wt % 45 45 total composition MFR g/10 min 0.9 1.4 IV on soluble in Xylene at 25° C. dl/g 2.75 2.43 C₂ = ethylene; C₄ = 1-butene; * alculated

The polyolefin compositions were blended at 16% by extrusion under the previously described conditions with the additional components reported below:

-   -   20.8% by weight of Moplen EP300M heterophasic polypropylene,         which was commercially available from LyondellBasell;     -   36.7 by weight of Moplen EP500V ultra-high fluidity         polypropylene copolymer, which was commercially available from         LyondellBasell;     -   17% by weight of talc Luzennac jetfine 3CA; and     -   9.5 wt of a premix composition.

The talc filled stabilized blend was extruded under nitrogen atmosphere in a twin screw extruder Leistritz 27 mm (length/diameter ratio of screws: 40) in the following conditions:

-   -   Rotation speed: 350 rpm;     -   Extruder output: 25 kg/hour;     -   Melt temperature: 240° C.

The properties of the resulting final composition are reported in Table 3.

Properties Norm Unit EX 1 Comp EX 2 MFR 230/2.16 ISO 1133 g/10‘ 20.3 20.1 Ash content 1 h, 625° C. ISO 3451/1 % 17.9 17.1 Flexural Modulus ISO 178 and N/mm2 1688 1677 (E-Modul) ISO 1873-2. Charpy Notched Impact ISO 179/1eA kJ/m2 20.9 18.4 23° C. And Charpy Notched Impact ISO 1873-2 kJ/m2 7.1 6.3 0° C. Charpy Notched Impact kJ/m2 3.84 2.9 −30° C. Gloss 60°, N127 GME 60413 G 1.3 1.3 Scratch resistance GME 60280 dL* 1.6 2.2 (10N), N127 Scratch resistance GME 60280 dL* 0.8 1.5 (10N), N111 

What is claimed is:
 1. A polyolefin composition comprising: A) 5-35% by weight of a propylene homopolymer containing 10% by weight or less of a fraction soluble in xylene at 25° C. (XS_(A)) the amount of the fraction XS_(A) being referred to the weight of (A); B) 20-50% by weight of an ethylene homopolymer containing 5% by weight or less of a fraction soluble in xylene at 25° C. (XS_(B)), the amount of the fraction XS_(B) being referred to the weight of (B); and C) 30-60% by weight of a terpolymer of ethylene, propylene and 1-butene derived units containing from 45% to 65% by weight of ethylene units and from 15% to 38% by weight of 1-butene units; and containing from 30% to 85% by weight of a fraction soluble in xylene at 25° C. (XS_(C)), the amount of the ethylene units, the 1-butene units, and the fraction XS_(C) being referred to the weight of (C); the amounts of (A), (B) and (C) being referred to the total weight of (A)+(B)+(C), the sum of the amount of (A)+(B)+(C) being 100 wt %.
 2. The polyolefin composition according to claim 1, wherein: Component (A) ranges from 10% by weight to 30% by weight; Component (B) ranges from 25% by weight to 45% by weight; and Component (C) ranges from 35% by weight to 55% by weight.
 3. The polyolefin composition according to claim 1, wherein Component (A) ranges from 15% by weight to 23% by weight; Component (B) ranges from 30% by weight to 40% by weight; and Component (C) ranges from 40% by weight to 50% by weight.
 4. The polyolefin composition according to claim 1, wherein in component (A), the fraction soluble in xylene at 25° C. (XSA) is 8 wt % or less.
 5. The polyolefin composition according to claim 1, wherein component (B) is an ethylene homopolymer having 4 wt % or less of a fraction soluble in xylene at 25° C. (XSB).
 6. The polyolefin composition according to claim 1, wherein component (C) is terpolymer of ethylene, propylene and 1-butene containing from 48% to 62% by weight of ethylene units and from 18% to 33% by weight of 1-butene units.
 7. The polyolefin composition according to claim 1, wherein component (A) has a melt flow rate (230° C./2.16 kg) ranging between 50 and 200 g/10 min.
 8. The polyolefin composition according to claim 1, wherein components (A)+(B) blended together have a melt flow rate (230° C./2.16 kg) ranging between 0.1 and 70 g/10 min.
 9. The polyolefin composition according to claim 1, wherein component (A) has a melt flow rate (230° C./2.16 kg) ranging between 80 and 170 g/10 min.
 10. The polyolefin composition according to claim 1, wherein component (B) has a melt flow rate (230° C./2.16 kg) ranging between 0.1 and 30 g/10 min.
 11. The polyolefin composition according to claim 1, wherein the ethylene homopolymer (B) has a density (determined according to ISO 1183 at 23° C.) of from 0.940 to 0.965 g/cm³.
 12. The polyolefin composition according to claim 1, having a melt flow rate (230° C./2.16 kg) between from 0.8 to 20.0 g/10 min.
 13. An impact modifier comprising the polyolefin composition according to claim
 1. 14. (canceled)
 15. (canceled)
 16. An article of manufacture comprising the polyolefin composition according to claim 1, wherein the article is selected from the group consisting of films and molded articles. 